深圳邦克尔是沙伯基础Lexan PC HFD4271深圳市邦克尔塑胶原料有限公司专业代理销售,提供HFD4271物性表、HFD4271注塑技术支持、最新HFD4271价格,充足HFD4271现货库存。

产品详情

品牌:Sabic 
品名:Lexan
品类:PC
牌号:HFD4271      HFD4271物性表.pdf
色号:HFD4271-2B5D008,HFD4271-5R6D021,HFD4271-7B1D132,HFD4271-7B6D019,HFD4271-7N1D096,HFD4271-7R5D043,HFD4271-7R7D071,HFD4271-7T2D352,HFD4271-8B8D044,HFD4271-8B9D107,HFD4271-8N9D097,HFD4271-9B5D005,HFD4271-9B5D006,HFD4271-BL2G176,HFD4271-BR3H002,HFD4271-BR4H001,HFD4271-BR4H002,HFD4271-BR6G154,HFD4271-BR6G157,HFD4271-BR6G174,HFD4271-BR6G184,HFD4271-GN5G135,HFD4271-GN5G136,HFD4271-GY1G374,HFD4271-GY3G111,HFD4271-GY3G407,HFD4271-GY4G362,HFD4271-GY5G385,HFD4271-GY6G346,HFD4271-GY7G341,HFD4271-GY7G605,HFD4271-GY7H035,HFD4271-GY8H004,HFD4271-OR5G086,HFD4271-RD7G060,HFD4271-RD8G026,HFD4271-WH9G212,HFD4271-WH9G229,HFD4271-WH9G355,HFD4271-WH9G614,HFD4271-WH9G786,HFD4271-WH9G797,HFD4271-WH9G804
中文简介:HFD4271是一种10%玻璃填充,高流动性,抗冲击改性,注塑级,设计用于高流动性和卓越的表面外观。HFD4271具有增强的脱模性,冲击延展性和宽广的色彩空间。
英文简介:LEXAN HFD4271 is a 10% glass filled, high flow, impact modified, injection moldable grade designed for high flow and superior surface appearance. HFD4271
has enhanced mold release, impact ductility and broad color space.

沙伯基础一级Sabic商,邦克尔可以为您提供HFD4271最新资讯:
Sabic Lexan PC HFD4271的最新报价,您可以直接致电0755-27105659。
Sabic Lexan PC HFD4271物性表及其相关报告,您可以邮件到polymer@bak99.com。
如您对我们的Sabic
Lexan PC HFD4271有任何疑问需要技术支持,敬请直接联系沙伯基础邦克尔。

LEXAN™ HFD4271 resin 物性表
基本信息
填料/增强材料
  • 玻璃纤维增强材料, 10% 填料按重量
添加剂
  • 冲击改性剂
  • 脱模
特性
  • 流动性高
  • 外观良好
  • 延展性
加工方法
  • 注射成型

物理性能 额定值 单位制 测试方法
比重
    -- 1.26 g/cm³ ASTM D792
    -- 1.25 g/cm³ ISO 1183
熔流率(熔体流动速率) (300°C/1.2 kg) 15 g/10 min ASTM D1238
溶化体积流率(MVR) (300°C/1.2 kg) 14.0 cm³/10min ISO 1133
收缩率 内部方法
    流动 : 3.20 mm 0.20 到 0.30 % 内部方法
    横向流动 : 3.20 mm 0.40 到 0.50 % 内部方法
吸水率 ISO 62
    饱和, 23°C 0.13 % ISO 62
    平衡, 23°C, 50% RH 0.040 % ISO 62

机械性能 额定值 单位制 测试方法
拉伸模量 1 3700 MPa ASTM D638
抗张强度
    屈服 2 53.0 MPa ASTM D638
    屈服 59.0 MPa ISO 527-2/5
    断裂 3 39.0 MPa ASTM D638
    断裂 48.0 MPa ISO 527-2/5
伸长率
    屈服 4 3.0 % ASTM D638
    屈服 3.0 % ISO 527-2/5
    断裂 9.0 % ISO 527-2/5
弯曲模量 5(50.0 mm 跨距) 3300 MPa ASTM D790
弯曲强度 6(屈服, 50.0 mm 跨距) 95.0 MPa ASTM D790

冲击性能 额定值 单位制 测试方法
简支梁缺口冲击强度 7 ISO 179/1eA
    -30°C 9.0 kJ/m² ISO 179/1eA
    23°C 18 kJ/m² ISO 179/1eA
简支梁无缺口冲击强度 8 ISO 179/1eU
    -30°C 100 kJ/m² ISO 179/1eU
    23°C 110 kJ/m² ISO 179/1eU
悬壁梁缺口冲击强度
    23°C 230 J/m ASTM D256
    -30°C 9 9.0 kJ/m² ISO 180/1A
    23°C 10 20 kJ/m² ISO 180/1A
无缺口悬臂梁冲击
    23°C 1700 J/m ASTM D4812
    -30°C 11 68 kJ/m² ISO 180/1U
    23°C 12 93 kJ/m² ISO 180/1U
装有测量仪表的落镖冲击 (23°C, Total Energy) 36.0 J ASTM D3763

热性能 额定值 单位制 测试方法
载荷下热变形温度 ASTM D648
    0.45 MPa, 未退火, 3.20 mm 131 °C ASTM D648
    1.8 MPa, 未退火, 3.20 mm 125 °C ASTM D648
维卡软化温度 135 °C ISO 306/B120
Ball Pressure Test (125°C) Pass IEC 60695-10-2
线形热膨胀系数
    流动 : -40 到 40°C 4.0E-5 cm/cm/°C ASTM E831
    流动 : 23 到 80°C 3.0E-5 cm/cm/°C ISO 11359-2
    横向 : -40 到 40°C 7.0E-5 cm/cm/°C ASTM E831
    横向 : 23 到 80°C 8.0E-5 cm/cm/°C ISO 11359-2
RTI Elec 80.0 °C UL 746
RTI Imp 80.0 °C UL 746
RTI 80.0 °C UL 746

可燃性 额定值 测试方法
UL 阻燃等级 (0.400 mm) HB UL 94

注射 额定值 单位制
干燥温度 121 °C
干燥时间 3.0 到 4.0 hr
干燥时间,最大 48 hr
建议的最大水分含量 0.020 %
建议注射量 40 到 60 %
料筒后部温度 266 到 288 °C
料筒中部温度 277 到 299 °C
料筒前部温度 288 到 310 °C
射嘴温度 282 到 304 °C
加工(熔体)温度 288 到 310 °C
模具温度 71.1 到 93.3 °C
背压 0.345 到 0.689 MPa
螺杆转速 40 到 70 rpm
排气孔深度 0.025 到 0.076 mm

备注
1 . 5.0 mm/min
2 . 类型 1, 5.0 mm/min
3 . 类型 1, 5.0 mm/min
4 . 类型 1, 5.0 mm/min
5 . 1.3 mm/min
6 . 1.3 mm/min
7 . 80*10*3 sp=62mm
8 . 80*10*3 sp=62mm
9 . 80*10*3
10 . 80*10*3
11 . 80*10*3
12 . 80*10*3