Product Chinese name: polyphenylene ether + PS
Product English name: PPO
Brand name and grade: NORYL GFN2
Common name: PPO
Brand name and grade: NORYL GFN2
Chinese name of chemical: polyphenylene ether + PS
English name of chemical: PPO
Supplier: Sabic (Sabic Innovative Plastics)
Product packaging: 25KG/BAG
Origin: America, China
Product description
Noryl PPO GFN2 Physical Properties Table
20% glass fiber reinforced. DTUL (Deflection Temperature Under Load): 290F (143C). UL94 rated HB value. Equipment applications in contact with water: pump casings and impellers. Also used for motor casings, etc.
Property/Characteristics
TYPICAL PROPERTIES | |||
MECHANICAL/mechanical properties | Value/value | Unit/unit | Standard/standard |
Tensile Stress, brk, Type I / Tensile Stress, Break, Type I, 5 mm/min | 90 | MPa | ASTM D 638 |
Tensile Strain, brk, Type I / Tensile StrainLong, Break, Type I, 5 mm/min | 2.6 | % | ASTM D 638 |
Tensile Modulus / Tensile Modulus, 5 mm/min | 6200 | MPa | ASTM D 638 |
Flexural Stress, yld / Flexural Strength, Yield, 1.3 mm/min, 50 mm span | 160 | MPa | ASTM D 790 |
Flexural Modulus / Flexural Modulus, 1.3 mm/min, 50 mm span | 5800 | MPa | ASTM D 790 |
Hardness, Rockwell / Rockwell hardness L | 106 | – | ASTM D 785 |
Tensile Stress, break / Tensile Stress, break, 5 mm/min | 97 | MPa | ISO 527 |
Tensile Strain, break / tensile elongation, break, 5 mm/min | 2.5 | % | ISO 527 |
Tensile Modulus / Tensile Modulus, 1 mm/min | 7070 | MPa | ISO 527 |
Flexural Stress, yield / Bending Strength, Yield, 2 mm/min | 167 | MPa | ISO 178 |
Flexural Modulus / Flexural Modulus, 2 mm/min | 6540 | MPa | ISO 178 |
IMPACT/impact performance | Value/value | Unit/unit | Standard/standard |
Izod Impact, unnotched / Unnotched Izod Impact, 23°C | 650 | J/m | ASTM D 4812 |
Izod Impact, notched / Notched Izod Impact Strength, 23°C | 119 | J/m | ASTM D 256 |
Izod Impact, notched / Izod notched impact strength, -40°C | 96 | J/m | ASTM D 256 |
Instrumented IMPACT Total Energy / Instrumented IMPACT Total Energy, 23°C | 22 | J | ASTM D 3763 |
Izod Impact, notched / Izod notched impact strength 80*10*4 +23°C | 11 | kJ/m2 | ISO 180/1A |
Charpy Impact, notched, 23°C | 11 | kJ/m2 | ISO 179/2C |
THERMAL/thermal performance | Value/value | Unit/unit | Standard/standard |
HDT (Heat Deflection Temperature), 0.45 MPa, 3.2 mm, unannealed | 140 | °C | ASTM D 648 |
HDT (Heat Deflection Temperature), 1.82 MPa, 3.2mm, unannealed (not annealed) | 135 | °C | ASTM D 648 |
HDT (Heat Deflection Temperature), 0.45 MPa, 6.4 mm, unannealed | 143 | °C | ASTM D 648 |
HDT (Heat Deflection Temperature), 1.82 MPa, 6.4 mm, unannealed | 137 | °C | ASTM D 648 |
CTE (coefficient of linear expansion), -40°C to 40°C, flow | 2.89E-05 | 1/°C | ASTM E 831 |
CTE (coefficient of linear expansion), -40°C to 40°C, xflow (transverse direction) | 8.26E-05 | 1/°C | ASTM E 831 |
Vicat Softening Temp, Rate / Vicat softening temperature, grade B/50 | 143 | °C | ISO 306 |
Vicat Softening Temp, Rate / Vicat softening temperature, grade B/120 | 146 | °C | ISO 306 |
HDT (heat distortion temperature)/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 143 | °C | ISO 75/Be |
HDT (heat distortion temperature)/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 137 | °C | ISO 75/Ae |
Relative Temp Index, Elec / Relative Thermal Index, Electrical Properties | 90 | °C | UL 746B |
Relative Temp Index, Mech w/impact / Relative Thermal Index, Mechanical Impact | 90 | °C | UL 746B |
Relative Temp Index, Mech w/o impact / relative thermal index, non-mechanical impact performance | 90 | °C | UL 746B |
PHYSICAL/Physical Properties | Value/value | Unit/unit | Standard/standard |
Specific Gravity / specific gravity | 1.2 | – | ASTM D 792 |
Water Absorption / water absorption, 24 hours | 0.06 | % | ASTM D 570 |
Mold Shrinkage / shrinkage, flow, 3.2 mm | 0.2 – 0.5 | % | SABIC Method |
Melt Flow Rate / melt flow rate,, 300°C/5.0 kgf | 9 | g/10min | ASTM D 1238 |
Melt Volume Rate / Melt Volume Flow Rate, MVR at 300°C/5.0 kg | 8 | cm3/10 min | ISO 1133 |
ELECTRICAL/Electrical Performance | Value/value | Unit/unit | Standard/standard |
Dielectric Strength, in oil / Dielectric Strength, in oil, 3.2 mm | 16.5 | kV/mm | ASTM D 149 |
Relative Permittivity / relative permittivity, 50/60 Hz | 2.86 | – | ASTM D 150 |
Dissipation Factor / Dissipation Factor, 50/60 Hz | 0.0008 | – | ASTM D 150 |
Arc Resistance, Tungsten / arc resistance {PLC} | 7 | PLC Code | ASTM D 495 |
Hot Wire Ignition / Hot Wire Ignition {PLC) | 4 | PLC Code | UL 746A |
High Voltage Arc Track Rate / High Voltage Arc Tracking Rate {PLC} | 4 | PLC Code | UL 746A |
High Ampere Arc Ign, surface / High Ampere Arc Ign, Surface {PLC} | 4 | PLC Code | UL 746A |
FLAME CHARACTERISTICS/flame characteristics | Value/value | Unit/unit | Standard/standard |
UL Recognized, 94HB Flame Class Rating / Flame Retardant Level (3) | 1.47 | mm | UL 94 |
Oxygen Index / Limiting Oxygen Index (LOI) | 26 | % | ASTM D 2863 |
UV-light, water exposure/immersion / UV-light exposure, water-resistant/immersion | F1 | – | UL 746C |
The following are the physical properties of Saudi Arabia-SABIC plastic NORYL PPE/PS GFN2: NORYL GFN2